Fabrication of Corrosion-Resistant Superhydrophobic Coatings and Impermeable Porous Structures Using Fluorinated Microemulsions Containing Thermally Decomposable Surfactants

In this work, a series of fluorinated microemulsions were synthesized using thermally decomposable N-dodecyl-N,N-dimethylamine N-oxide (LDAO) as surfactant. Then, polybutylene terephthalate nonwoven fabrics (PBT) were coated with microemulsion and heat-treated. Superhydrophobic and oil-repellent modified PBT with WCA (water contact angle) of about 152°, a sliding angle of about 2.1°, and oil repellency grade of 8 were prepared. The effect of surfactants on the surface wettability of hydrophobic materials was analyzed by TG-DTA, XPS, and WCA tests. The results show that surfactants decrease the WCA of hydrophobic materials, but LDAO can eliminate this effect by heat treatment. The anti-corrosion and permeability of LDAO coatings were compared with those of conventional fluorinated coatings through degradation and anti-permeability tests. It was shown that the LDAO fluorinated superhydrophobic coating is more resistant to corrosion by chemical solutions and significantly improves the impermeability of porous materials. Anti-fouling and self-cleaning tests showed excellent anti-fouling and self-cleaning properties on several common substrate surfaces modified with LDAO fluorinated microemulsions. It is expected that these new LDAO fluorinated microemulsions have promising applications in the preparation of corrosion-resistant surfaces and impermeable structures.

» Author: Bin Zhang

» Reference: doi: 10.3390/coatings14091176

» Publication Date: 11/09/2024

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es