A synergistic effect of Li-B-Si glass and La-B on low-temperature sintering of BaO-0.15ZnO-4TiO2 dielectric ceramic

In the present work, the synergistic effect of Li2O-B2O3-SiO2 glass (LBS) and La2O3-B2O3 (LaB) addition on the wetting behavior, activation energy, phase composition, microstructure and microwave dielectric properties of the BaO-0.15ZnO-4TiO2 ceramic (Ba-Zn-Ti) has been investigated to understand the low temperature mechanism of the sintering kinetic. The results show that co-doping with LBS and LaB decreases the activation energy and therefore accelerates the sintering process of the Ba-Zn-Ti due to the liquid phase formed at a low sintering temperature. Moreover, the co-doping of LBS and LaB restrains the appearance of BaTi(BO3)2 caused by the reaction of Ba-Zn-Ti and LBS, which has a deleterious effect on the densification and microwave dielectric properties of Ba-Zn-Ti. With LBS and LaB co-doped, the sintering temperature of Ba-Zn-Ti significantly dropped from 1150°C to 850–900°C and remained excellent microwave dielectric properties.

» Author: Shuxin Duan, Enzhu Li, Hongyu Yang, Bin Tang, Ying Yuan, Hongcai He, Shuren Zhang

» Reference: Ceramics International, Volume 43, Issue 9

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es