Vacuum Tribological Properties of W-S-N Coatings Synthesized by Direct Current Magnetron Sputtering

This work deals with the investigation of the tribological performance of DC magnetron sputtered W-S-N coatings under vacuum atmosphere, as part of the exploration of multi-environment sliding properties of W-S-N solid lubricants. This study is part of the systematic testing of W-S-N solid lubricants in different environments, especially vacuum, which is often ignored. The trend is to test sliding properties in dry N2 by considering it as replacement of vacuum environment testing. This approach is not appropriate. In this work, a set of coatings was synthesized with N-alloying content in the range of 0–25.5 at.%. A maximum S/W ratio of 1.47 was observed for the pure WSx coating. A maximum hardness of 8.0 GPa was observed for 23 at.% of N-alloying. The coating with the lowest N content (14.6 at.%) displayed the lowest friction, specific wear rate and wear scar depth under vacuum conditions. Despite superior sliding performance at room temperature (35% humidity), 200 °C and dry nitrogen conditions, the performance of the WSN12.5 coating deteriorated vacuum environment.

» Author: Talha Bin Yaqub

» Reference: doi: 10.3390/coatings12111646

» Publication Date: 30/10/2022

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es