Ni-based mesoporous Ce0.8Zr0.2O2 catalyst with enhanced low-temperature performance for CO2 methanation

The Ni/Ce0.8Zr0.2O2 catalysts with different Ni doping amounts (5?wt%, 10?wt%, 15?wt%, 20?wt%, and 25?wt%) are prepared by the impregnation technique and used as CO2 methanation catalysts in this work. The effects of various Ni doping loading on CO2 methanation catalytic performance at low temperatures were investigated in this catalytic system. The results show that the catalyst with 15?wt% Ni doping shows the best catalytic performance. Since the heated sintering of Ni nanoparticles was prevented efficiently by CO2 methanation, these mesoporous catalysts exhibit excellent stability. Therefore, the catalyst is expected to be an efficient CO2 methanation catalyst at low temperatures.

» Author: Bin Chen, Jian Qiu, Liang Xu, Yan Cui

» Publication Date: 01/11/2022

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es