Study of morphology and electrical properties of indium zinc oxide-modified kenaf fiber

Indium zinc oxide (IZO) was successfully deposited onto kenaf fibers (KFs) by a dip-coating method. The novel aspect of this study was the investigation of the electrical conductivity of the resulting indium zinc oxide-modified kenaf fiber (KF-IZO) by emphasizing on its morphology and the dipping rate used for dip-coating. KF was alkalized using a 5% sodium hydroxide (NaOH) solution. The dipping rate was varied from 1 to 30mm/s. KF-IZO was then annealed at a temperature of 150°C for 4h. A modified four-probe method employing a copper metal attachment plate was used to evaluate the electrical properties of KF-IZO. A dipping rate of 5mm/s, which yielded the highest electrical conductivity of 11.81S/mm, was found to be optimum. Scanning Electron Microscope/Energy Dispersive Using X-Ray (SEM-EDX) analysis of KF-IZO revealed that the IZO film was uniformly coated on the KF substrates, and no significant thermal damage was observed. KF-IZO showed the potential to be used in smart textiles, electrostatic discharge protection, and as a reinforcement in composites.

» Author: Edynoor bin Osman, Toshihiro Moriga, Kei-ichiro Murai, Mohd Warikh bin Abd Rashid

» Reference: Industrial Crops and Products, Volume 100

» Publication Date: 01/06/2017

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es