A pulp foam with highly improved physical strength, fire-resistance and antibiosis by incorporation of chitosan and CPAM

Bio-inspired borate cross-linked pulp foam (PF) with high porosity and low density can be widely used in many fields. However, PF is flammable, and lack of mechanical strength and antibacterial activity. To solve these issues, an ultra-strong PF was prepared by incorporation of chitosan and cationic polyacrylamide (CPAM). Results showed that the obtained PF exhibited highly improved mechanical properties (the compressive strength (485?kPa at a strain of 50%) was over 6 times higher compared with the borate cross-linked PF without chitosan and CPAM, and it was even higher than most of the reported cellulose-based porous materials). Also, the prepared PF has good performance on fire-retardance (hard to light), thermal insulation, antibiosis and sound absorption, due to the synergistic actions of borate, chitosan and CPAM. Additionally, spent liquor in preparing PF could be fully recycled, and thus this sustainable approach has potential for large-scale production of high-performance PF.

» Author: Meiyan Wu, Guang Yu, Wei Chen, Sheng Dong, Yiran Wang, Chao Liu, Bin Li

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es