Deformation Behavior and Dynamic Recrystallization of Ti?22Al?25Nb Alloy in 750?990??C

Ti?22Al?25Nb is a representative of Ti2AlNb alloys with excellent comprehensive properties, which has great application prospects in the aerospace field. High temperature tensile plastic deformation behavior and dynamic recrystallization process of Ti?22Al?25Nb alloy are researched during 750 ? 990 ?C in this paper. From 750 to 870 ?C, plasticity is gradually improved with temperature rising, and the fracture mode is crack aggregation. From 900 to 930 ?C, content of B2 phase increases and plasticity is significantly improved, because crack along the grain is suppressed by combined precipitation of three phases B2+O+?2 at grain boundaries with large areas. From 960 to 990 ?C, the alloy is mainly composed of B2 phase and has best plastic deformation performance. Fully dynamic recrystallization of B2 phase happens at 990 ?C. Texture strength is strengthened by intense plastic deformation, but it is weakened by dynamic recrystallization subsequently.This article is protected by copyright. All rights reserved.

» Author: Huang Shuhui, Shao Bin, Xu Wenchen, Shan Debin, Guo Bin, Zong Yingying

» Reference: doi:10.1002/adem.201901231

» Publication Date: 12/12/2019

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es