Synthesis of highly sinterable Yb:Lu2O3 nanopowders via spray co-precipitation for transparent ceramics

Highly sinterable Yb:Lu2O3 nano-powders without hard agglomeration were synthesized via a highly efficient spray co-precipitation method. The effects of the spray speeds on morphology and composition of the powders were investigated. The results showed that the composition and dispersion of precursor powders changed with the spray speed. When the spray speed reached 40?mL/min, the particles were spherical and showed higher uniformity. The pure phase Yb:Lu2O3 powder was obtained after calcining at 1000??C for 2?h. The calcined powders were ball milled and dry-formed to prepare green body. Then the Yb:Lu2O3 transparent ceramic was fabricated by vacuum sintering at 1500??C for 8?h and further hot isostatic pressing in an argon atmosphere.. The in-line optical transmittance of Yb:Lu2O3 transparent ceramic reached 82.05%@1000?nm and 81.08%@400?nm, respectively, and it had submicron level average grain size, which is an effective way to improve the optical properties of the transparent ceramic.

» Author: Linlin Dong, Mingzhen Ma, Wei Jing, Tao Xu, Kang Bin, Ruisong Guo

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es