Microstructure, properties and thermal stability of W/B4C multilayer coating synthesized by ion beam sputtering

Microstructure, hardness and toughness as well as the thermal stability of W/B4C multilayer coating synthesized by ion beam sputtering were investigated. The results show well-defined layered structure and uniform monolayers can be found in the as-deposited multilayer coatings with various period thickness at fixed period ratio (W:B4C?=?1:1.5). The crystallinity of W layer and the roughness of W/B4C interfaces are changed as the period thickness increasing. It can be concluded that the nano multilayer coatings have superior strengthening and toughening effects. The hardness of as-deposited (W5.2nm/B4C7.6nm)20, (W10.5nm/B4C15.8nm)10 and (W14.5nm/B4C21.5nm)7 coatings is greatly enhanced and higher than that of pure B4C coating, and the toughness of W/B4C multilayer coating is significantly higher than that of pure B4C coating. Subsequently, the investigations about thermal stability of (W10.5nm/B4C15.8nm)10 multilayer coatings indicate that the layered structural is stable when the heat treatment temperature is lower than 500?°C. With increasing of heat treatment temperature, the oxidation of W layer and the formation of WO3 compounds were found. The nano layered structure was dramatically destroyed accompanying severe oxidation and slight carbonization when the temperature increase up to 600?°C. The hardness of (W10.5nm/B4C15.8nm)10 multilayer coating increases up to 37?GPa when the coating is heat treated below 500?°C, while it declined sharply when the coating is heat treated at 600?°C due to the a degradation of layered structure. In addition, the toughness of the multilayer coatings monotonously decreases with the increase of heat treatment temperature.

» Author: Bin Huang, Wei Le, Yuetang Wang, Xian Luo, Yanqing Yang

» Reference: 10.1016/j.apsusc.2018.09.077

» Publication Date: 15/01/2019

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es