Simultaneously enhancing the IFSS and monitoring the interfacial stress state of GF/epoxy composites via building in the MWCNT interface sensor

This paper presents an effective technology that could simultaneously enhance the interfacial shear strength (IFSS) and monitor the interfacial stress state between glass fiber and epoxy vinyl ester resin (GF/epoxy). Muiti-walled carbon nanotube (MWCNT) was added to aqueous surfactant solution and dispersed by ultrasonic. Subsequently, MWCNT was deposited on GF surface by physical vapor deposition. The results show that the sensing performance of the developed sensor was dependence on MWCNT solution concentration, interface length, ultrasonic dispersion duration, and immersion cycles. Fiber-bundle pull-out tests show that IFSS of GF/epoxy was enhanced by incorporating MWCNT into the interphase. By measuring resistance change of the MWCNT sensor, the interfacial evolution behaviour was monitored during the pull-out test. The results indicate that the presented technology can be successfully used for in-situ sensing the accumulated interfacial damage and simultaneously enhancing the IFSS of GF/epoxy composites.

» Author: Bin Yang, Fu-Zhen Xuan, Hongshuai Lei, Zhenqing Wang, Yanxun Xiang, Kang Yang, Xiaojun Tang, Wenyan Liang

» Reference: Composites Part A: Applied Science and Manufacturing, Volume 112

» Publication Date: 01/09/2018

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es