Effects of chain-extending stabilizer on bioplastic poly(lactic acid)/polyamide blends compatibilized by reactive extrusion

The immiscible bio-plastic blend of poly(lactic acid) (PLA) and polyamide11 (PA11 or Nylon11) was compatibilized, using a catalyzed the ester-amide interchange chemical reaction during reactive extrusion. The effects of screw configuration on mixing and reaction optimization were explored. It was found that effective mixing and minimized degradation were achieved when kneading elements were installed only near the die end of the extruder rather than near the beginning of the melt section. However, significant degradation of PLA could not be avoided during processing, which led to a decrease in mechanical strength of blend. To prevent the molecular weight reduction, tris(nonylphenyl) phosphite (TNPP) stabilizer was introduced to improve the thermal stability of PLA matrix. Improvement to both tensile strength and elongation were achieved in the resulting PLA/PA11/TsOH/TNPP blend.

» Author: JeongIn Gug, Margaret J. Sobkowicz, James Soule, Bin Tan

» Reference: Polymer Degradation and Stability

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es