The electrical conductivity (?) and oxygen diffusivity of the typical Ruddlesden-Popper oxide Sr3Fe2O7-? were investigated with the variation of oxygen partial pressure, P(O2), and temperatures, and thus the results were discussed based on its defect structure. The ? increases with the increase of P(O2) and a positive slope of log ? depend on P(O2) is close to 1/4 with the small polaron conduction, where the mobility ? P are between 0.01 and 0.02 cm2 V?1 s?1 regardless of temperature and P(O2). Oxygen diffusivity derived from the electrical conductivity relaxation (ECR) after an abrupt change of P(O2) increased with the increase P(O2) and temperature. A new pulse isotope 18O-16O exchange (PIE) at 623–773K was carried in order to rapidly determine the tracer oxygen surface reaction coefficient. The numerical relationship of oxygen diffusivity measured by ECR and PIE measurements was successfully established by the ambipolar diffusion theory and defect chemical analysis.

» Author: Yihan Ling, Tianmin Guo, Xiaozhen Zhang, Riyan Achmad Budiman, Yoshinobu Fujimaki, Takashi Nakamura, Bin Lin, Tatsuya Kawada, Koji Amezawa

» Reference: Ceramics International, Volume 43, Issue 18

» More Information

« Go to Technological Watch



AIMPLAS Instituto Tecnológico del Plástico

C/ Gustave Eiffel, 4
(València Parc Tecnològic) - 46980
PATERNA (Valencia) - SPAIN

PHONE

(+34) 96 136 60 40

EMAIL

Project Management department - Sustainability and Industrial Recovery
life-future-project@aimplas.es